NON-FERROUS METAL REFINERY

Isaac Peral,12 – Pol.Ind. Sudoest – 08960 Sant Just Desvern

Barcelona, Spain. Tel: +34 933 714 400 Fax: +34 933 714 550

VAT: A-08258949 urgilsa@urgilsa.com

Presentation

URGIL S.A. is a Spanish company with more than 30 years of experience in brass ingot and brass bar manufacture.

Our main customers are specialised in brass fittings, faucets and valve fittings production since we offer a wide range of possibilities for any type of alloy produced according to customer requirements.

We offer a good brass product which means we have excellent results in casting fluidity, stamping, machining, chrome plating and polishing.

In view of our fine selection of raw materials, we are able to offer a high quality brass line, with excellent results in terms of smelting-casting, machining, polishing and chrome-plating.

All our products are specially designed for die-casting as well as pressure die-casting and they comply with the international standards for the official certification of finished products.

Our company is part of a holding able to carry out the whole process of production of faucets, brass fittings and valves. Our good quality material is very well appreciated all around the world and 30% of our output is being exported to EUROPE, SINGAPORE, MALAYSIA, AUSTRALIA and CHINA. Moreover, our material has been used in the setting-up of several Production Lines for High Quality Faucets, like in ZIBO, providing service and technical and technological assistance for the normal operation of these production lines.

Products Designation

1. BRASS INGOT, EN 1982 CuZn37Pb2Ni1AlFe-B ( CB753S ) TAPES (faucets)“ T ” TYPE

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Ni Mn Si P Sb

Max. 60,00 2,50 Rest 0,80 0,80 0,70 1,20 0,10 0,05 0,02 0,05

Min. 59,00 1,80 Rest 0,50 0,45 0,50

Brass ingot for the manufacture of brass fittings with casting die.

Taps, ornamental pieces, fittings, faucets ,etc.

10-11 Kg 15-18 Kg

Die-cast ingot Continuous cast ingot

2. BRASS INGOT, EN 1982 CuZn39Pb1Al-B ( CB754S ) INJECTION, “ I ” TYPE

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Ni Mn Si P

Max. 59,80 2,40 Rest 0,70 0,80 0,50 0,60 0,10 0,05 0,02

Min. 59,40 1,80 Rest 0,40

Brass ingot for the manufacture of brass fittings with low pressure molding.

Taps, ornamental pieces, fittings,hinges, etc.

10-11 Kg 15-18 Kg

Die-cast ingot Continuous cast ingot

3. BRASS INGOT, EN 1982 CuZn39Pb1AlB-B (CB755S) LOW PRESSURE , “ BPU”TYPE

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Mn Ni Si

Max. 60,5 1,70 Rest 0,20 0,30 0,65 0,05 0,20 0,03

Min. 59,0 1,20 Rest 0,05 0,40

Brass ingot for the manufacture of brass fittings, faucets, with casting die

or low pressure molding. Taps, ornamental pieces, fittins, etc.

10-11 Kg 15-18 Kg

Die-cast ingot Continuous cast ingot

4. BRASS INGOT, “ R ” TYPE

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Ni Mn Si

Max. 75 6,5 Rest 1,90 1,50 0 0,90 0 0

Min. 65 4,5 Rest 0,80 0,70 0 0,40 0 0

Does not conform to any standard.

Mix this material with Zamak(Zn+Al) obtain a brass that useful to make many pieces.

The mix are 10-20% according to chemical composition of every furnace.

18-21 Kg

5. BRASS INGOT, “ 2R ” TYPE

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Ni Mn Si Sb

Max. 61 4,5 Rest 1,80 1,10 1 1 0 0 0,05

Min. 57 2,6 Rest 1 0,60 0,4 0,35 0 0 0.18

Does not conform to any standard.

This material is a brass that useful to make many pieces.

18-21 Kg

6. ROUND BRASS BAR (forging), CuZn40Pb2 EN-12165 CW617N

CHEMICAL COMPOSITION

Cu Pb Zn Fe Sn Al Mn Ni As

Max. 59,0 2,5 Rest < 0,3 < 0,3 < 0,05 --- < 0,3 ---

Min. 57,0 1,6

LONG. 2800-3200 mm

EXTRUSIONED AND GAGED FOR FORGING. Round brass bar for manufacturing brass fittings with hot forging. Brass fittings and connection elements for pipes.

Æ16,17,18,19,20,21,22,23,24,25,26,28,30,32,35,40,42,45,50, ±0.05mm.

Æ55,60 ±0.8mm no-gaged, directly from extrusion.